Jotun Penguard FC is a high build, two-pack epoxy coating that can be used as a topcoat in an epoxy paint system or as a single coat system on steel and concrete. Penguard FC should be used in areas where an epoxy finish is acceptable and ideally where there is little UV light penetration.
Available from SML Paints in over 300 colours
Jotun Penguard FC is a high build, two-pack epoxy coating that can be used as a topcoat in an epoxy paint system or as a single coat system on steel and concrete. Penguard FC should be used in areas where an epoxy finish is acceptable and ideally where there is little UV light penetration.
Available from SML Paints in over 300 colours
| Feature | Details |
|---|---|
| Brand | Jotun |
| Paint Protection | Anti-Corrosive |
| Paint Type | Topcoat |
| Paint Components | 2-Pack |
| Ease of Use | 3. Good |
| Substrate Suitability | Stainless Steel, Mild Steel, GRP, Galvanised Steel, Concrete, Aluminium |
| Surface Adhesion | 2. Very Good |
| Above / Below Waterline | Above Water |
| Water Resistance | 2. Very Good |
| Abrasion Resistance | 2. Very Good |
| Chemical Resistance | 2. Very Good |
| Solvent Resistance | 2. Very Good |
| Interior / Exterior Use | Exterior, Interior |
| UV Resistance | 4. Fair |
| Gloss Level | 3. Semi-gloss |
| Gloss Retention | 4. Fair |
| Colour Retention | 4. Fair |
| Flexibility | 3. Good |
| Application Method | Airless Spray, Brush, Roller |
| Recommended Coats (Brush / Roller) | 1-2 |
| Chemical Composition | Epoxy |
| Brand Range | Penguard |
| Brush or Roller Coverage Rate (m2 / L) | 8 |
| Cured for Service 10C (days) | 8 |
| Cured for Service 23C (days) | 4 |
| Dry to Overcoat 10C (hours) | 15 |
| Dry to Overcoat 23C (hours) | 7.5 |
| Full Curing Time 10C (days) | 8 |
| Full Curing Time 23C (days) | 4 |
| Max Dry Film Thickness per Coat (microns) | 200 |
| Max Overcoating Time without Sanding (days) | 90 |
| Min Dry Film Thickness per Coat (microns) | 80 |
| Pot Life 10C (hours) | 3 |
| Pot Life 23C (hours) | 2 |
| Product Type | Paint |
| Self-Priming | No |