Jotun Tankguard HB is a two-component, high-build epoxy coating with excellent resistance to a wide range of chemicals and solvents. It can be used as a primer, mid-coat, or finish coat in both atmospheric and immersed environments, making it suitable for properly prepared carbon steel, galvanized steel, stainless steel, and concrete substrates. Typical applications include internal linings for offshore, onshore, and buried tanks and pipes, as well as marine coatings for grey water, drilling mud, brine, and crude oil tanks.
Available from SML Paints in 20L grey or pink options
Jotun Tankguard HB is a two-component, high-build epoxy coating with excellent resistance to a wide range of chemicals and solvents. It can be used as a primer, mid-coat, or finish coat in both atmospheric and immersed environments, making it suitable for properly prepared carbon steel, galvanized steel, stainless steel, and concrete substrates. Typical applications include internal linings for offshore, onshore, and buried tanks and pipes, as well as marine coatings for grey water, drilling mud, brine, and crude oil tanks.
Available from SML Paints in 20L grey or pink options
Select an Option Below
| Feature | Details |
|---|---|
| Brand | Jotun |
| Paint Protection | Tank Coatings |
| Paint Type | Universal Coating |
| Paint Components | 2-Pack |
| Ease of Use | 3. Good |
| Substrate Suitability | Galvanised Steel, Aluminium, Concrete, GRP, Mild Steel, Stainless Steel |
| Surface Adhesion | 1. Excellent |
| Water Resistance | 2. Very Good |
| Abrasion Resistance | 2. Very Good |
| Chemical Resistance | 1. Excellent |
| Solvent Resistance | 1. Excellent |
| Gloss Level | 5. Matt |
| Application Method | Airless Spray, Brush, Roller |
| Recommended Coats (Brush / Roller) | 2-3 |
| Chemical Composition | Epoxy |
| Brand Range | Tankguard |
| Brush or Roller Coverage Rate (m2 / L) | 8 |
| Cured for Service 10C (days) | 14 |
| Cured for Service 23C (days) | 7 |
| Dry to Overcoat 10C (hours) | 24 |
| Dry to Overcoat 23C (hours) | 6 |
| Full Curing Time 10C (days) | 14 |
| Full Curing Time 23C (days) | 7 |
| Max Dry Film Thickness per Coat (microns) | 160 |
| Max Overcoating Time without Sanding (days) | 21 |
| Min Dry Film Thickness per Coat (microns) | 80 |
| Pot Life 10C (hours) | 12 |
| Pot Life 23C (hours) | 8 |
| Product Type | Paint |
| Self-Priming | No |